Aluminium Bronze Bolts and Nuts
UNS C61300 Nickel Aluminium bronze Hex Bolt, stud and fasteners manufacturer in India

Material |
ASTM Standards & Grades |
Size Range |
Aluminium Bronze |
ASTM B 111 C60800/ ASME SB 111 C 60800 / CW200 / C61400 / EN 12451 CuAL5AS / C95400 / C62300 / C62400 / C61800 / C62500 / C95900 / C95200 / CuAL11Ni5Fe5, BS1400-AB1/ AB2, BS2874 CA103 / CA104/ CW303G / CW300G |
1/4" to 2" |
Grades of Aluminium Bronze Nut Bolt | |
---|---|
DEFSTAN 02-833 (NES 833) | BS B23 |
CW307G | C63000 |
C63200 |
Aluminium Bronze fasteners available in following grades:
- Aluminium bronze CA 104 BS2874
- Aluminium bronze NES833 PART II
- Aluminium bronze C63000
- Aluminium bronze CW33G
- Aluminium bronze AB2 BS1400
Aluminium Bronze Bolts group
- Contains less than 8% Aluminium (Single phase alloys)
- Contains 8 to 11% Aluminium. Grade CA105, CA104. - Two-phase (duplex) alloys
- Aluminium-Silicon alloys - The low magnetic permeability
- Aluminium alloys -The Copper-Manganese
Aluminium Bronze Fasteners equivalents
CDA |
ASTM |
ASARCON |
SAE |
AMS |
Federal |
Military |
Other |
---|---|---|---|---|---|---|---|
C95400 |
B505 |
QQ-C-390, G5; QQ-B-671, CLASS 3 |
MIL-B-16033, CLASS 3 |
Aluminium Bronze 9C |
|||
C95400 |
B505 |
QQ-C-390, G5; QQ-B-671, CLASS 3 |
MIL-B-16033, CLASS 3 |
Aluminium Bronze 9C |
|||
C63000 |
B150-12 |
J461 J463 |
4640 |
QQ-C-465B AMD1 |
Other Bronze Bolts Grades
Aluminium Bronze | CA104 | Al 10% Ni5% Fe5% |
Phosphor Bronze | PB102 | Sn 5% P 0.2% |
Silicon Bronze | CS101 | Si 3% Mn1% |
Gunmetal | LG2 | Sn 5% Pb5% Zn5% |
Aluminium Bronze - cast | AB2 | Al 10% Ni5% Fe3% |
Aluminium Bronze Fasteners Chemical Composition
Chemical Composition Limits |
||||
Weight % |
Cu |
Al |
Fe |
Ni |
CA 104 |
Rem |
8.5 / 11.0 |
4.0 / 5.5 |
4.0 / 5.5 |
Mechanical Properties of Aluminium Bronze Bolts and Nuts
Material |
0.2% Proof Stress (N/mm² ) |
Tensile Strength (N/mm² ) |
Elongation % |
Hardness (HV) |
CA 104 |
420-500 |
720-820 |
25-15 |
200-240 |
Physical Properties Aluminium Bronze Nuts & Bolts
US Customary |
Metric |
|
---|---|---|
Melting Point - Liquidus |
1930° F |
1054° C |
Melting Point - Solidus |
1895° F |
1035° C |
Density |
0.274 lb/in3 at 68° F |
7.58 gm/cm3 at 20° C |
Specific Gravity |
7.58 |
7.58 |
Electrical Conductivity |
7% IACS at 68° F |
0.041 MegaSiemens/cm at 20° C |
Thermal Conductivity |
22.60 Btu · ft/(hr · ft2 · °F) at 68° F |
39.1 W/m at 20° C |
Coefficient of Thermal Expansion |
9.0 · 10-6 per °F (68°-572° F) |
15.5 · 10-6 per °C (20°-300° C) |
Specific Heat Capacity |
0.090 Btu/lb/°F at 68° F |
377.1 J/kg at 293° C |
Modulus of Elasticity in Tension |
17500 ksi |
120650 MPa |
Modulus of Rigidity |
6400 ksi |
44130 MPa |